Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 350 - 450 | mPa.s | MT-CU025V |
| Solid Content | 62 - 66 | % | MT-CU001C |
| Gel Time at 20°C + 1% MEKP50 | 45 - 55 | minutes | RS.08.G |
| Delta at 20°C + 1% MEKP50 | 8-15 | minutes | RS.08.G |
| Exothermic peak at 20°C + 1% MEKP50 | 155 - 185 | °C | RS.08.G |
| Specific weight at 20°C | 1,13 | g/cm3 | — |
| Value | Units | Test Method / Conditions | |
| Tensile strength at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 70 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 4000 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 135 | MPa | ISO 178/B (2010) |
| Flexural modulus at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 4000 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 64 | °C | ISO 75 -2A (2013) |
| Barcol Hardness at 25°C at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 45 | — | ASTM D 2583 (2007) |
| Elongation at break at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 2,5 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperatur