Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 69 - 73 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 3 rpm 20 | 1850 - 2150 | mPa.s | MT-CU025V |
| Gel Time at 25°C + 0,2% Co 6% + 2% AAP | 13 - 16 | minutes | RS.08.G |
| Delta at 25°C + 0,2% Co 6% + 2% AAP | 4:00 - 6:30 | minutes | RS.08.G |
| Exothermic peak at 25°C + 0,2% Co 6% + 2% AAP | 145 - 170 | °C | RS.08.G |
| Acidity at 25°C + 0,2% Co 6% + 2% AAP | 18 - 25 | mg KOH/g | MT-CU001I |
| Specific weight at 20°C | 1,15 | g/cm3 | — |
| Value | Units | Test Method / Conditions | |
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 140 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 66 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3200 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 46 | °C | ISO 75 -2A (2013) |
| Glass transition at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 56 | °C | ASTM E 1545 (2011) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 38 | — | ASTM D 2583 (2007) |
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 6,1 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature