Features & Benefits
- Materials Features
- Product Highlights
- Good adhesion to PMMA
- Low exothermic peak
- Low styrene emission
- Preaccelerated
- Thixotropic
- With catalyst indicator
Applications & Uses
- Applications
- Application Method
- Compatible Polymers & Resins
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 1,06 | g/cm3 | — |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 230 - 330 | mPa.s | MT-CUT25V |
| Solid Content | 52 - 56 | % | MT-CU001C |
| Gel Time at 25°C + 1,5% MEKP50 | 14 - 18 | minutes | RS.08.G |
| Delta at 25°C + 1,5% MEKP50 | 11-15 | — | RS.08.G |
| Exothermic peak at 25°C + 1,5% MEKP50 | 120 - 150 | °C | RS.08.G |
| Value | Units | Test Method / Conditions | |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 30 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 1700 | MPa | ISO 527 (2012) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 45 | °C | ISO 75 -2A (2013) |
| Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 54 | °C | ASTM E 1545 (2011) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 7,0 | % | ISO 527 (2012) |
Safety & Health
- Product Safety
As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating., Stir the resin before use, without use air bubbles
Storage & Handling
- Shelf Life
- 3 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature