Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Clear unaccelerated
- Light stabilized
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 65 - 69 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 680 - 840 | mPa.s | MT-CU023V |
| Gel Time at 85°C + 0,77% Trx K90 | 35 - 55 | sec | RS.08.G |
| Curing Time at 85°C + 0,77% Trx K90 | 120 - 160 | sec | RS.08.G |
| Exothermic peak at 85°C + 0,77% Trx K90 | 205 - 235 | °C | RS.08.G |
| Acidity at 85°C + 0,77% Trx K90 | 23 - 30 | mg KOH/g | MT-CU001I |
| Specific weight at 20°C | 1,14 | g/cm3 | — |
| Value | Units | Test Method / Conditions | |
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 130 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 75 | MPa | ISO 527 (2012) |
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 43 | — | ASTM D 2583 (2007) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3600 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 63 | °C | ISO 75 -2A (2013) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3,6 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature