Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Clear unaccelerated
Applications & Uses
- Markets
- Applications
Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 61 - 65 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 380 - 460 | mPa.s | MT-CU025V |
| Curing Time at 80°C + 0,2% Co 6% + 2% TBPB HAM1 | 5:10 - 6:00 | minutes | RS.03.G |
| Exothermic peak at 80°C + 0,2% Co 6% + 2% TBPB HAM1 | 195 - 210 | °C | RS.03.G |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Value | Units | Test Method / Conditions | |
| Tensile strength at 80°C for 1h in H20 +2h at 100°C +1h at 100°C | 65 | MPa | ISO 527 (2012) |
| Tensile Modulus at 80°C for 1h in H20 +2h at 100°C +1h at 100°C | 4100 | MPa | ISO 527 (2012) |
| Flexural strength at 80°C for 1h in H20 +2h at 100°C +1h at 100°C | 100 | MPa | ISO 178/B (2010) |
| Flexural modulus at 80°C for 1h in H20 +2h at 100°C +1h at 100°C | 3950 | MPa | ISO 178/B (2010) |
| HDT at 80°C for 1h in H20 +2h at 100°C +1h at 100°C | 53 | °C | ISO 75 -2A (2013) |
| Glass transition at 80°C for 1h in H20 +2h at 100°C +1h at 100°C | 68 | °C | ASTM E 1545 (2011) |
| Barcol Hardness at 25°C at 80°C for 1h in H20 +2h at 100°C +1h at 100°C | 43 | — | ASTM D 2583 (2007) |
| Elongation at break at 80°C for 1h in H20 +2h at 100°C +1h at 100°C | 2,0 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature