Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Medium reactivity
- Clear unaccelerated
Applications & Uses
- Markets
- Applications
Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 670 - 720 | mPa.s | MT-CU025V |
| Solid Content | 66 - 70 | % | MT-CU001C |
| Gel Time at 25°C + 0,2% Co 6% + 2% mix MEKP/AAP | 34 - 38 | minutes | RS.08.G |
| Delta at 25°C + 0,2% Co 6% + 2% mix MEKP/AAP | 5-12 | minutes | RS.08.G |
| Exothermic peak at 25°C + 0,2% Co 6% + 2% mix MEKP/AAP | 150 - 180 | °C | RS.08.G |
| Specific weight at 20°C | 1,14 | g/cm3 | — |
| Value | Units | Test Method / Conditions | |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 135 | MPa | ISO 178/B (2010) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 43 | — | ASTM D 2583 (2007) |
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3900 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3900 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 70 | MPa | ISO 527 (2012) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 59 | °C | ISO 75 -2A (2013) |
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 2,5 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 5 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature