Features & Benefits
- Materials Features
- Product Highlights
- Good transparence
- Clear unaccelerated
- Light stabilized
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Specific weight at 20°C | 1,12 | g/cm3 | — |
Brookfield Viscosity at 25°C, sp 2 rpm 20 | 200 - 230 | mPa.s | MT-CU025V |
Solid Content | 58 - 61 | % | MT-CU001C |
Gel Time at 25°C + 0,2% Co 6% + 1,5%MEKP50 | 5:30 - 5:50 | minutes | RS.08.G |
Delta at 25°C + 0,2% Co 6% + 1,5%MEKP50 | 7:20 - 8:00 | minutes | RS.08.G |
Exothermic peak at 25°C + 0,2% Co 6% + 1,5%MEKP50 | 190 - 210 | °C | RS.08.G |
Acidity at 25°C + 0,2% Co 6% + 1,5%MEKP50 | 24 - 29 | mg KOH/g | MT-CU001I |
Value | Units | Test Method / Conditions | |
Flexural strength at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 130 | MPa | ISO 178/B (2010) |
Tensile strength at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 65 | MPa | ISO 527 (2012) |
Tensile Modulus at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 3900 | MPa | ISO 527 (2012) |
Flexural modulus at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 3800 | MPa | ISO 178/B (2010) |
HDT at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 84 | °C | ISO 75 -2A (2013) |
Glass transition at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 103 | °C | ASTM E 1545 (2011) |
Barcol Hardness at 25°C at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 44 | — | ASTM D 2583 (2007) |
Elongation at break at 23°C for 24h/ at 100°C for +2h /at 100°C for +1h | 2,0 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 3 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature