Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Good transparence
- Clear unaccelerated
- Light stabilized
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 59 - 63 | % | MT-CU001C |
| Exothermic peak at 25°C + 0,2% Co 6% + 1,5% MEKP50 | 170 - 200 | °C | RS.08.G |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 260 - 310 | mPa.s | MT-CU025V |
| Reactivity at 25°C | % | % | MEKP50 |
| Gel Time at 25°C + 0,2% Co 6% + 1,5% MEKP50 | 4:00 - 5:30 | minutes | RS.08.G |
| Delta at 25°C + 0,2% Co 6% + 1,5% MEKP50 | 7:30 - 10:00 | minutes | RS.08.G |
| Value | Units | Test Method / Conditions | |
| Curing Cycle at 23°C (at 100°C) | 24 (2) | hr | — |
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 4000 | MPa | ISO 527 (2012) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 45 | — | ASTM D 2583 (2007) |
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 4000 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 70 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 130 | MPa | ISO 178/B (2010) |
| Glass transition at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 80 | °C | ASTM E 1545 (2011) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 70 | °C | ISO 75 -2A (2013) |
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 2,0 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 3 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature