Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Clear unaccelerated
- Light stabilized
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 57 - 61 | % | MT-CU001C |
| Specific weight at 20°C | 1,09 | g/cm3 | — |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 150 - 190 | mPa.s | MT-CU025V |
| Gel Time at 60°C + 0,15% Co 1% + 1,5% MIKP | 17:40 - 19:40 | minutes | RS.03.G |
| Curing Time at 60°C + 0,15% Co 1% + 1,5% MIKP | 21 - 27 | minutes | RS.03.G |
| Exothermic peak at 60°C + 0,15% Co 1% + 1,5% MIKP | 190 - 210 | °C | RS.03.G |
| Acidity at 60°C + 0,15% Co 1% + 1,5% MIKP | 21 - 28 | mg KOH/g | MT-CU001I |
| Value | Units | Test Method / Conditions | |
| Tensile strength at 60°C for 2h in H2O/ + 2h a 100°C /+ 1h at 100°C | 75 | MPa | ISO 527 (2012) |
| Tensile Modulus at 60°C for 2h in H2O/ + 2h a 100°C /+ 1h at 100°C | 3800 | MPa | ISO 527 (2012) |
| Flexural strength at 60°C for 2h in H2O/ + 2h a 100°C /+ 1h at 100°C | 130 | MPa | ISO 178/B (2010) |
| Flexural modulus at 60°C for 2h in H2O/ + 2h a 100°C /+ 1h at 100°C | 3700 | MPa | ISO 178/B (2010) |
| HDT at 60°C for 2h in H2O/ + 2h a 100°C /+ 1h at 100°C | 80 | °C | ISO 75 -2A (2013) |
| Glass transition at 60°C for 2h in H2O/ + 2h a 100°C /+ 1h at 100°C | 90 | °C | ASTM E 1545 (2011) |
| Barcol Hardness at 25°C at 60°C for 2h in H2O/ + 2h a 100°C /+ 1h at 100°C | 46 | — | ASTM D 2583 (2007) |
| Elongation at break at 60°C for 2h in H2O/ + 2h a 100°C /+ 1h at 100°C | 3,0 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature