| Value | Units | Test Method / Conditions | |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 350 - 450 | mPa.s | MT-CUT25V |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Gel Time at 25°C + 0,2% Co 6% + 2% mix MEKP/AAP | 21:00 - 23:00 | minutes | RS.08.G |
| Curing Time at 25°C + 0,2% Co 6% + 2% mix MEKP/AAP | 26:50 - 32:50 | — | RS.08.G |
| Exothermic peak at 25°C + 0,2% Co 6% + 2% mix MEKP/AAP | 180 - 210 | °C | RS.08.G |
| Acidity at 25°C + 0,2% Co 6% + 2% mix MEKP/AAP | 13 - 21 | mg KOH/g | MT-CU001I |
| Solid Content | 65,5 - 68 | % | MT-CU001C |
| Value | Units | Test Method / Conditions | |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 115 | MPa | ISO 178/B (2010) |
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3300 | MPa | ISO 178/B (2010) |
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3500 | MPa | ISO 527 (2012) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 65 | MPa | ISO 527 (2012) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 44 | — | ASTM D 2583 (2007) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 94 | °C | ISO 75 -2A (2013) |
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 2,6 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature
- Use before reported shelf-life