Features & Benefits
- Product Highlights
- Low styrene emission
- Preaccelerated
- Medium reactivity
- Thixotropic
Applications & Uses
- Applications
- Application Method
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 57 - 61 | % | MT-CU001C |
| Specific weight at 20°C | 1,10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 350 - 750 | mPa.s | MT-CUT23V |
| Gel Time at 23°C + 1,5% MEKP50 | 10-12 | minutes | MT-CU151R |
| Peak at 23°C + 1,5% MEKP50 | 15 - 20 | minutes | MT-CU151R |
| Exothermic peak at 23°C + 1,5% MEKP50 | 120 - 140 | °C | MT-CU151R |
| Value | Units | Test Method / Conditions | |
| Tensile strength at 140°C for 16h /+ 2 h at 90°C | 45 | MPa | ISO 527 (2012) |
| Tensile Modulus at 140°C for 16h /+ 2 h at 90°C | 3550 | MPa | ISO 527 (2012) |
| Flexural strength at 140°C for 16h /+ 2 h at 90°C | 90 | MPa | ISO 178 (2011) |
| Flexural modulus at 140°C for 16h /+ 2 h at 90°C | 3500 | MPa | ISO 178 (2011) |
| HDT at 140°C for 16h /+ 2 h at 90°C | 65 | °C | ISO 75 -2A (2013) |
| Elongation at break at 140°C for 16h /+ 2 h at 90°C | 1,55 | % | ISO 527 (2012) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature