Features & Benefits
- Product Highlights
- Low styrene emission
- Preaccelerated
- Very good glass wet-out
Applications & Uses
- Applications
- Application Method
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 650 - 800 | mPa.s | MT-CU025V |
| Solid Content | 74 - 78 | % | MT-CU001C |
| Gel Time | 10-14 | minutes | MT-CU151R |
| Exothermic peak | 65 - 85 | °C | MT-CU151R |
| Specific weight at 20°C | 1,55 | g/cm3 | — |
| Reactivity at 23°C | + 1,5 | % | MEKP50 |
| Peak (23°C) | 24 - 34 | — | — |
| Value | Units | Test Method / Conditions | |
| Elongation at break | 1,1 | % | ISO 527 (2012) |
| Curing Cycle at 40°C + 2 h at 90°C (at 120°C for HDT)) | 16 (2) | hr | — |
| Tensile strength | 35 | MPa | ISO 527 (2012) |
| Tensile Modulus | 3450 | MPa | ISO 527 (2012) |
| Flexural strength | 70 | MPa | ISO 178 (2011) |
| Flexural modulus | 3500 | MPa | ISO 178 (2011) |
| HDT | 74 | °C | ISO 75 -2A (2013) |
Safety & Health
- Product Safety
The final Fire resistance properties could change following the final structure of the piece and its use's condition. It will be necessary to verify the final properties on a prototype before industrial production.
Storage & Handling
- Shelf Life
- 4 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature