Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Low styrene content
- Preaccelerated
- Thixotropic
Applications & Uses
- Applications
- Application Method
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 1,10 | g/cm3 | — |
| Solid Content | 62 - 66 | % | MT-CU001C |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 700 - 900 | mPa.s | MT-CUT23V |
| Reactivity at 23°C | 2 | % | MEKP50 |
| Gel Time | 32 - 38 | minutes | MT-CU127R |
| Exothermic peak | 70 - 110 | °C | MT-CU127R |
| Peak (23°C) | 75 - 95 | — | — |
| Value | Units | Test Method / Conditions | |
| Tensile strength | 50 | MPa | ISO 527 (2012) |
| Curing Cycle at 40°C + 2 h at 90°C (at 120°C for HDT) | 16 (2) | hr | — |
| Tensile Modulus | 3100 | MPa | ISO 527 (2012) |
| Flexural strength | 95 | MPa | ISO 178 (2011) |
| Flexural modulus | 2950 | MPa | ISO 178 (2011) |
| HDT | 75 | °C | ISO 75 -2A (2013) |
| Elongation at break | 2,8 | % | ISO 527 (2012) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature