Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Medium reactivity
- Medium flexibility and elasticity
- Medium viscosity
Applications & Uses
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 58 - 62 | % | MT-CU001C |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Gel Time at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 14 - 17 | minutes | MT-CU152R |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 330 - 430 | mPa.s | MT-CU023V |
| Peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 26 - 32 | minutes | MT-CU152R |
| Exothermic peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 145 - 165 | °C | MT-CU152R |
| Value | Units | Test Method / Conditions | |
| Curing Cycle at 23°C (at 100°C) | 24 (2) | hr | — |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 76 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3470 | MPa | ISO 527 (2012) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3.9 | % | ISO 527 (2012) |
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 137 | MPa | ISO 178 (2011) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3640 | MPa | ISO 178 (2011) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 73 | °C | ISO 75 -2A (2013) |
Storage & Handling
- Shelf Life
- 9 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature