Features & Benefits
- Product Highlights
- With catalyst indicator
- Low reactivity
- Low styrene emission
- Low exothermic peak
- Preaccelerated
- Thixotropic
Applications & Uses
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Solid Content | 56 - 60 | % | MT-CU001C |
Specific weight at 20°C | 1,10 | g/cm3 | — |
Brookfield Viscosity at 23°C, sp 4 rpm 50 | 600 - 1000 | mPa.s | MT-CUT23V |
Gel Time at 23°C + 1% MEKP50 | 10:30 - 13:30 | minutes | MT-CU151R |
Peak at 23°C + 1% MEKP50 | 20 - 26 | — | MT-CU151R minutes |
Exothermic peak at 23°C + 1% MEKP50 | 95 - 115 | °C | MT-CU151R |
Value | Units | Test Method / Conditions | |
Elongation at break at 40°C for 16h | 2,3 | % | ISO 527 (2012) |
Curing Cycle at 40°C (120°C for HDT)) | 16 (+2) | hr | — |
Tensile strength at 40°C for 16h | 57 | MPa | ISO 527 (2012) |
Tensile Modulus at 40°C for 16h | 3715 | MPa | ISO 527 (2012) |
Flexural strength at 40°C for 16h | 98 | MPa | ISO 178 (2011) |
Flexural modulus at 40°C for 16h | 3630 | MPa | ISO 178 (2011) |
HDT at 40°C for 16h /+ 2 h at 120°C | 64 | °C | ISO 75 -2A (2013) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature