- With catalyst indicator
- Low styrene emission
- Low exothermic peak
- Preaccelerated
- Medium reactivity
- Thixotropic
Applications & Uses
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Specific weight at 20°C | 1,09 | g/cm3 | — |
Brookfield Viscosity at 23°C, sp 2 rpm 50 | 400 - 500 | mPa.s | MT-CUT23V |
Solid Content | 55.5 - 59.5 | % | MT-CU001C |
Gel Time at 23°C + 1,5% MEKP50 | 14:30 - 17:30 | minutes | MT-CU151R |
Peak at 23°C + 1,5% MEKP50 | 23 - 29 | — | MT-CU151R |
Exothermic peak at 23°C + 1,5% MEKP50 | 130 - 150 | °C | MT-CU151R |
Value | Units | Test Method / Conditions | |
Elongation at break at 40°C for 16h / + 2 h at 90°C | 1,97 | % | ISO 527 (2012) |
Tensile strength at 40°C for 16h / + 2 h at 90°C | 68 | MPa | ISO 527 (2012) |
Tensile Modulus at 40°C for 16h / + 2 h at 90°C | 4161 | MPa | ISO 527 (2012) |
Flexural strength at 40°C for 16h / + 2 h at 90°C | 119 | MPa | ISO 178 (2011) |
Flexural modulus at 40°C for 16h / + 2 h at 90°C | 4300 | MPa | ISO 178 (2011) |
HDT at 40°C for 16h / + 2 h at 90°C | 80 | °C | ISO 75 -2A (2013) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature