Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- High reactivity
- Medium viscosity
Applications & Uses
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 61 - 65 | % | MT-CU001C |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Gel Time at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 8-12 | minutes | MT-CU152R |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 500 - 600 | mPa.s | MT-CU023V |
| Peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 15 - 21 | minutes | MT-CU152R |
| Exothermic peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 165 - 185 | °C | MT-CU152R |
| Value | Units | Test Method / Conditions | |
| Elongation at break at 40°C for 16h /+ 2 h at 90°C | 1,25 | % | ISO 527 (2012) |
| Tensile strength at 40°C for 16h /+ 2 h at 90°C | 40 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h /+ 2 h at 90°C | 3475 | MPa | ISO 527 (2012) |
| Flexural strength at 40°C for 16h /+ 2 h at 90°C | 115 | MPa | ISO 178 (2011) |
| Flexural modulus at 40°C for 16h /+ 2 h at 90°C | 3770 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h /+ 2 h at 120°C | 106 | °C | ISO 75 -2A (2013) |
Storage & Handling
- Shelf Life
- 9 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature