Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- High reactivity
- Low styrene emission
- Low viscosity
- Pigmented
- Preaccelerated
Applications & Uses
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 57 - 61 | % | MT-CU001C |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 220 - 320 | mPa.s | MT-CU023V |
| Gel Time at 23°C + 1,5% MEKP50 | 34 - 40 | minutes | MT-CU151R |
| Peak at 23°C + 1,5% MEKP50 | 42 - 52 | minutes | MT-CU151R |
| Exothermic peak at 23°C + 1,5% MEKP50 | 165 - 185 | °C | MT-CU151R |
| Value | Units | Test Method / Conditions | |
| Elongation at break at 40°C for 16h / + 2 h at 90°C | 1,25 | % | ISO 527 (2012) |
| Flexural strength at 40°C for 16h / + 2 h at 90°C | 115 | MPa | ISO 178 (2011) |
| Tensile strength at 40°C for 16h / + 2 h at 90°C | 40 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h / + 2 h at 90°C | 3475 | MPa | ISO 527 (2012) |
| Flexural modulus at 40°C for 16h / + 2 h at 90°C | 3770 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h / + 2 h at 120°C | 106 | °C | ISO 75 -2A (2013) |
Safety & Health
- Product Safety
As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
Storage & Handling
- Shelf Life
- 4 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature