Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Low reactivity
- Low exothermic peak
- Preaccelerated
- Thixotropic
Applications & Uses
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 1,12 | g/cm3 | — |
| Solid Content | 55 - 59 | % | MT-CU001C |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 700 - 900 | mPa.s | MT-CUT23V |
| Gel Time at 23°C + 1,5% MEKP50 | 34 - 40 | minutes | MT-CU151R |
| Peak at 23°C + 1,5% MEKP50 | 65 - 75 | minutes | MT-CU151R |
| Exothermic peak at 23°C + 1,5% MEKP50 | 60 - 80 | °C | MT-CU151R |
| Value | Units | Test Method / Conditions | |
| Elongation at break at 40°C for 16h | 2,75 | % | ISO 527 (2012) |
| Tensile strength at 40°C for 16h | 75 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h | 3884 | MPa | ISO 527 (2012) |
| Flexural strength at 40°C for 16h | 107 | MPa | ISO 178 (2011) |
| Flexural modulus at 40°C for 16h | 3503 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h /+2h for 120°C | 68 | °C | ISO 75 -2A (2013) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature