Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Fire retardand properties
- Good transparence
- Light stabilized
- Medium reactivity
- Preaccelerated
- Very good glass wet-out
- Very long shelf life
Applications & Uses
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 1,23 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 390 - 430 | mPa.s | MT-CU023V |
| Solid Content | 64 - 72 | % | MT-CU001C |
| Gel Time at 85°C + peroxydes | 2:00 - 2:40 | minutes | MT-CU026R |
| Curing Time at 85°C + peroxydes | 3:15 - 4:15 | minutes | MT-CU026R |
| Exothermic peak at 85°C + peroxydes | 208 - 223 | °C | MT-CU026R |
| Value | Units | Test Method / Conditions | |
| Tensile strength at 80°C for 16hrs / at 120°C for +2hrs | 33 | MPa | ISO 527 (2012) |
| Tensile Modulus at 80°C for 16hrs / at 120°C for +2hrs | 4080 | MPa | ISO 527 (2012) |
| Elongation at break at 80°C for 16hrs / at 120°C for +2hrs | 1 | % | ISO 527 (2012) |
| Flexural strength for at 80°C for 16hrs / at 120°C for +2hrs | 50 | MPa | ISO 178 (2011) |
| Flexural modulus at 80°C for 16hrs / at 120°C for +2hrs | 4070 | MPa | ISO 178 (2011) |
| HDT at 80°C for 16hrs / at 120°C for +2hrs | 75,5 | °C | ISO 75 -2A (2013) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature