Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Fire retardand properties
- Good aging resistance
- Good transparence
- Light stabilized
- Medium reactivity
- Preaccelerated
- Very good glass wet-out
Applications & Uses
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 1,10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 330 - 370 | mPa.s | MT-CU023V |
| Solid Content | 59 - 67 | % | MT-CU001C |
| Gel Time at 85°C + peroxydes | 1:50 - 2:50 | minutes | MT-CU026R |
| Curing Time at 85°C + peroxydes | 3:30 - 4:45 | — | MT-CU026R min:sec |
| Exothermic peak at 85°C + peroxydes | 195 - 210 | °C | MT-CU026R |
| Value | Units | Test Method / Conditions | |
| Tensile Modulus at 40°C for 16h | 3532 | MPa | ISO 527 (2012) |
| Flexural strength at 40°C for 16h | 100 | MPa | ISO 178 (2011) |
| Flexural modulus at 40°C for 16h | 3070 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h / at 120C for+2h | 70 | °C | ISO 75 -2A (2013) |
| Elongation at break at 40°C for 16h | 4,3 | % | ISO 527 (2012) |
| Tensile strength at 40°C for 16h | 55,6 | MPa | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature