- They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties.
- Lotrene® Q1018 Series are suited for many applications in the field of consumer, agricultural, industrial, food or hygiene packaging, for example: collation shrink, liners, FFS bags, heavy duty sacks, refuse, tunnel films, mulching films.
- Additive Package
PRODUCT SLIP (ERUCAMIDE) (PPM) ANTIBLOCK (PPM) THERMAL STABILIZERS
Q1018N no no Yes (blown film) Q1018H 1500 3200 Yes (blown film) - Values indicated are target values. Actual values might differ from batch to batch.
- (The above properties are measured on a blown film under following parameters: Screw 45 mm, L/D 30, die gap 2.2 mm, output 30 kg/hr, mass temperature °210C, thickness 40 pm and BUR 2.5:1)
- Processing
Lotrene Q1018 Series can be processed at high output rates with moderate extrusion pressure, good bubble stability and gage control on blown film lines designed for LLDPE. Lotréne Q1018 Series can be blended with LDPE and other PE resins in order to improve film properties or process ability on conventional mono or co extrusion machines.
Properties
- Polymer Properties
- Film Properties
- Processing Properties
Value | Units | Test Method / Conditions | |
Crystalline Melting Point | 122.0 | °C | Internal |
Density (23°C) | 0.918 | g/cm³ | ASTM D792 |
Melt Flow Index (190°C /2.16 Kg) | 1.0 | g/10 min | ASTM D1238 |
Vicat Softening Point | 100.0 | °C | ASTM D1525 (A120) |
Value | Units | Test Method / Conditions | |
Elongation at Break (TD) | 800.0 | % | ASTM D882 |
Elongation at Break (TD) | 850.0 | % | ASTM D882 |
Gloss (45°C) | 60.0 | — | ASTM D2457 |
Haze | 11.0 | % | ASTM D1003 |
Impact Strength (F 50) | 150.0 | g | ASTM D1709 |
Secant Modulus (%1 MD) | 215.0 | MPa | ASTM D882 |
Secant Modulus (%1 TD) | 245.0 | MPa | ASTM D882 |
Tear Resistance (MD) | 280.0 | g | ASTM D 1922 |
Tear Resistance (TD) | 480.0 | g | ASTM D 1922 |
Tensile Strength at Break (MD) | 38.0 | MPa | ASTM D882 |
Tensile Strength at Break (TD) | 33.0 | MPa | ASTM D882 |
Tensile Strength at Yield (MD) | 11.0 | MPa | ASTM D882 |
Tensile Strength at Yield (TD) | 11.0 | MPa | ASTM D882 |
Value | Units | Test Method / Conditions | |
Blow-Up Ratio | 2:1 to 3:1 | — | — |
Die Gap | min. 1.8 | mm | — |
Extrusion Temperatures | 180 - 220 | °C | — |
Melt Temperature | 200.0 | °C | — |
Regulatory & Compliance
- Certifications & Compliance
- Food Contact & Reach
Lotréne® polyethylene products manufactured by Qatar Petrochemical Company (QAPCO) Q.S.C. comply with US, EU and other food contact legislations. Limitations may apply. All QAPCO Lotréne products are complying with REACH Regulation 1907/2006/EC. The aims of this regulation are to improve the protection of human health and the environment through better and earlier identification of the intrinsic properties of chemical substances. Not suitable for pharmaceutical or medical applications.
Safety & Health
- Safety
Under normal conditions Lotrene® products do not present a toxic hazard through skin contact or inhalation.
Storage & Handling
- Handling & Storage
Polyethylene products should be stored in their original packaging or in clean appropriate silos. The products should be stored in a dry and well-ventilated area and should not be exposed to direct sunlight and/ or heat in any form since this may adversely affect their properties. As a general rule, our products should not be stored for more than three months from receipt date.