Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Composites Processing Methods
- Applications
- Lamborghini
- Callaway Golf
- Dodge Viper
Properties
- Color
- Physical Form
- Cured Properties
- Uncured Properties
| Value | Units | Test Method / Conditions | |
| Specific Gravity (Machined) | 1.45 | g/cc | ASTM D-792 |
| Flexural Strength (Machined) | 57,000 (393) | psi (MPa) | ASTM D-790 |
| Flexural Modulus (Machined) | 5.0 x106 (34.4) | psi (GPa) | ASTM D-790 |
| Tensile Strength (Machined) | 63,000 (434) | psi (MPa) | ASTM D-3039 |
| Tensile Modulus (Machined) | 6.0 x106 (41.3) | psi (GPa) | ASTM D-3039 |
| Glass Transition Temperature (Machined) | 288 (142) | °F (°C) TanDelta | ASTM D-7028 |
| Value | Units | Test Method / Conditions | |
| Color | Natural and Black | — | — |
| Areal Weight | 1272 | gms/m2 | — |
| Carbon Fiber Content (Nominal) | 55 | % | — |
| Carbon Fiber Length (Continuous) | 2 x 2 | twill | — |
Technical Details & Test Data
- Molding Suggestions
AMC® 8575 can be molded at temperatures in the range of 260-310°F, with 280°F suggested as a starting point. Cure times will be dependent on molding temperature and part thickness and will typically be 5-10 minutes. Detailed molding suggestions are available on request. Cool molded parts at ambient temperature. A cooling fixture may be needed depending on part thickness and geometry.
Packaging & Availability
- Packaging Type
Storage & Handling
- Shelf Life
- 3 Months (75°F)
- Precautions
AMC® 8575 contains carbon fibers and should be handled carefully in order to minimize skin contact. Molding areas should be well ventilated to minimize exposure to fumes. Presses must be provided with local exhaust to remove vapors from work areas. If adequate ventilation is not available, a respirator approved for removing organic vapor must be used. Care must be taken to prevent contact of carbon fibers with electrical equipment.