Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Labeling Claims
- Materials Features
- Features
- Next-Generation BMI Formulation Technology
- Lower Cost Equivalent to Industry-Standard Products
- Improved Durability – Compression-After-Impact
- Superior Hot-Wet Performance
- Continuous Service Temperature up to 400°F, Excursions to 500°F
- Excellent Fire, Smoke and Toxicity Performance
- Successfully passed the FAA 2000°F (Kerosene) Flame Test
- Autoclave, Compression Molding and Out-of-Autoclave Cure Products Available
- Available on Carbon, Glass or Quartz Fabrics and Carbon Uni-Weaves
- Reasonable Lead-Times and Min Order Quantities
- Qualified at Major Jet Engine OEM's
- Up to 450°F Service
- 375°F Cure with Multiple Options on Free Standing Post Cure Temp
Applications & Uses
- Markets
- Composites Processing Methods
Properties
- Physical Form
- Resin Properties
Value | Units | Test Method / Conditions | |
Glass Transition Temperature (no Post Cure) | 484 | °F | — |
Glass Transition Temperature (no Post Cure) | 251 | °C | — |
Glass Transition Temperature (w/Post Cure) | 530 | °F | — |
Glass Transition Temperature (w/Post Cure) | 277 | °C | — |
Cured Resin Density | 1.25 | g/cc | — |
Resin Flex Strength (170 MPa) | 24.7 | ksi | — |
Resin Flex Modulus (4.8 GPa) | 701 | ksi | — |
Resin Flex Strain to Failure | 3.6 | % | — |