Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Appearance
- Colorless
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Optical Properties
- Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Tensile Strength at Break | 60 | MPa | ASTM D 638 |
Tensile Strength at Yield | 50 | MPa | ASTM D 638 |
Tensile Modulus (0.2 in/min (5 mm/min)) | 3000 | MPa | ASTM D638 |
Elongation at Break | 2 | % | ASTM D 638 |
Yield Elongation | 2 | % | ASTM D638 |
Izod Notched Impact Strength (0.125 in / 3.175 mm) | 16 | J/m | ASTM D256 |
Izod Unnotched Impact Strength (0.125 in / 3.175 mm) | 181 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Melt Flow Rate - MFR (200°C/5.0 Kg) | 3 | g/10 min | ASTM D1238 |
Density | 1.09 | g/cm3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (264 psi, Unannealed, 0.5 in (12.7 mm)) | 85 | °C | ASTM D648 |
Vicat Temperature (0.125 in (3.175 mm)) | 102 | °C | ASTM D1525 |
Value | Units | Test Method / Conditions | |
Haze | 0.9 | % | ASTM D 1003 |
Light Transmittance | 92 | % | ASTM D 1003 |
Value | Units | Test Method / Conditions | |
Rear Temperature | 170-180 | °C | — |
Front Temperature | 200-210 | °C | — |
Maximum Recommended Temperature | 250 | °C | — |
Center Temperature | 180-190 | °C | — |