Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers Processing Methods
Properties
- Physical Properties
- Mechanical Properties
- Thermal Properties
| Value | Units | Test Method / Conditions | |
| Density (23 °C, 50 % RH) | 1.22 | g/cm³ | DIN EN ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Elongation at Break (50 mm/min 23 °C) | min. 50 | % | DIN EN ISO 527 |
| Flexural Modulus (2 mm/min 23 °C) | 2200 | MPa | DIN EN ISO 178 |
| Flexural Strength (2 mm/min 23 °C) | 80 | MPa | DIN EN ISO 178 |
| Flexural Strength at (3.5% Strain of the outer Fiber) | 70 | MPa | DIN EN ISO 178 |
| Impact Strength (Charpy) | n.b. | kJ/m² | DIN EN ISO 179/1eU |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 13 | kJ/m² | DIN EN ISO 179/1eA |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 52 | kJ/m² | DIN EN ISO 179/1eA |
| Tensile Modulus (1 mm/min 23 °C) | 2300 | MPa | DIN EN ISO 527 |
| Tensile Strength (50 mm/min 23 °C) | 57 | MPa | DIN EN ISO 527 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (B 50) | 125 | °C | DIN EN ISO 306 |
| Flammability own test) | HB | — | UL94 |
| Glow Wire Flammability Index (GWFI) | 800 | °C | DIN EN 60695-2-12 |
| Heat deflection temperature (HDT/A) | 94 | °C | DIN EN ISO 75-1 |
| Melt Mass-Flow Rate (MFR) | 30 | g/10 min | DIN EN ISO 1133 |
| Processing Shrinkage (220 °C, 10 kg) | 0.4 0.6 | % | DIN EN ISO 294-4 |
Regulatory & Compliance
Packaging & Availability
- Regional Availability