| Value | Units | Test Method / Conditions | |
| Density (23 °C, 50 % RH) | 1.12 | g/cm³ | DIN EN ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Elongation at Break (50 mm/min 23 °C) | min. 30 | % | DIN EN ISO 527 |
| Flexural Modulus (2 mm/min 23 °C) | 2550 | MPa | DIN EN ISO 178 |
| Flexural Strength (2 mm/min 23 °C) | 66 | MPa | DIN EN ISO 178 |
| Impact Strength (Charpy) | 40 | kJ/m² | DIN EN ISO 179/1eU |
| Impact Strength (Charpy) | 45 | kJ/m² | DIN EN ISO 179/1eU |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 10 | kJ/m² | DIN EN ISO 179/1eA |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 5 | kJ/m² | DIN EN ISO 179/1eA |
| Tensile Modulus (1 mm/min 23 °C) | 2500 | MPa | DIN EN ISO 527 |
| Tensile Strength (50 mm/min 23 °C) | 43 | MPa | DIN EN ISO 527 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (B 50) | 126 | °C | DIN EN ISO 306 |
| Flammability (own test) | HB | — | UL94 |
| Heat deflection temperature (HDT/A) | 65 | °C | DIN EN ISO 75-1 |
| Melt Mass-Flow Rate (MFR) | 16 | g/10 min | DIN EN ISO 1133 |
| Processing Shrinkage (220 °C, 10 kg) | 0.3 0.7 | % | DIN EN ISO 294-4 |