Value | Units | Test Method / Conditions | |
Water Absorption (23 °C, 50 % RH, 24 h) | 0.3 | % | DIN EN ISO 62 |
Density (23 °C, 50 % RH) | 1.09 | g/cm³ | DIN EN ISO 1133 |
Value | Units | Test Method / Conditions | |
Elongation at Break (50 mm/min 23 °C) | 30 | % | DIN EN ISO 527 |
Flexural Modulus (2 mm/min 23 °C) | 2050 | MPa | DIN EN ISO 178 |
Flexural Strength (2 mm/min 23 °C) | 66 | MPa | DIN EN ISO 178 |
Impact Strength (Charpy) | n.b. | kJ/m² | DIN EN ISO 179/1eU |
Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 15 | kJ/m² | DIN EN ISO 179/1eA |
Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 8.7 | kJ/m² | DIN EN ISO 179/1eA |
Tensile Modulus (1 mm/min 23 °C) | 2100 | MPa | DIN EN ISO 527 |
Tensile Strength (50 mm/min 23 °C) | 43 | MPa | DIN EN ISO 527 |
Value | Units | Test Method / Conditions | |
Flammability (own test) | HB | — | UL94 |
Heat deflection temperature (HDT/A) | 82 | °C | DIN EN ISO 75-1 |
Melt Mass-Flow Rate (MFR) | 24 | g/10 min | DIN EN ISO 1133 |
Processing Shrinkage (220 °C, 10 kg) | 0.3 0.6 | % | DIN EN ISO 294-4 |
Vicat Softening Temperature (B 50) | 94 | °C | DIN EN ISO 306 |