It is preferred to use desiccant dryers, at reduced temperatures and drying times. 150°F for 2 hours is a target with dew point between -20°F and -40°F. Too high of temperatures and drying times will burn out the fragrance. In the absence of a desiccant dryer, the injection molding machine hopper may be used. Tray dryers may also be used.
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Elongation (73.4°F, 50RH%) | 35 | % | ASTM D638 |
Izod Impact Strength of Notch (73.4°F, 50RH%) | 3.5 | ft-lb/in | ASTM D256 |
Accelerated Aging (72 Hrs. Wt. Lost, 180°F) | 1.2 | % | ASTM D706 |
Tensile Strength at Upper Yield (73.4°F, 50RH%) | 4800 | psi | ASTM D638 |
Flextural Strength at Yield (73.4°F, 50RH%) | 7500 | psi | ASTM D790 |
Flow Temperature | 320 | °F | ASTM D569 |
Modulus of Elasticity x 105 (in Flexture, 73.4°F, 50RH%) | 1.9 | psi | ASTM D790 |
Rockwell Hardness - R Scale (73.4°F, 50RH%) | 85 | — | ASTM D785 |
Soluble Matter lost (73.4°F) | 0.2 | % | ASTM D570 |
Specific Gravity (73.4°F, 50RH%) | 1.28 | — | ASTM D792 |
Water Absortion (24Hr Immersion, 73.4°F) Total | 2.3 | % | ASTM D570 |
Tensile Strength at Fracture (73.4°F, 50RH%) | 6300 | psi | ASTM D638 |
Deformation under load (cold flow) method A (Dry) Load 2000 psi (122°F) | 3 | % | ASTM D621 |
Tensile Strength at Fracture (158°F, 50RH%) | 3200 | psi | ASTM D638 |
Deformation under load (cold flow) method A (Dry) Load 1000 psi (122°F) | 1 | % | ASTM D621 |
Izod Impact Strength of Notch (-40°F, 50RH%) | 1.1 | ft-lb/in | ASTM D256 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Typical Molding Conditions
Scented Cellulose Acetate
Barrel Temp Starting Profile.Flow H2 Rear 420°- 450°F Center 420°- 450°F Front 420°- 450°F Nozzle 430°- 460°F Scented Cellulose Acetate Propionate
Barrel Temp Starting Profile.Flow H2 Root 300°- 310°F Rear - Root 310°- 320°F Rear - Center 320°- 330°F Center 345°- 355°F Front 375°- 395°F Nozzle 375°- 395°F Pressures
Flow H2 Moveable Half 1600 / 1200 PSIG Back Pressure 0 – 50 PSI - Mold Temperatures
- SOFT FLOWS BELOW MS - 100°F – 140°F
- HARDER FLOWS - 100°F – 180°F
- Cycle Times
- INJECTION (3) - 8 – 12 sec.
- BOOSTER - 6 – 12 sec.
- CURE - 40 – 70 sec.
- Tooling
The mold vent for the tool should be .002” to .003”. If this is not the case, mold temperatures could be elevated to help drive off volatiles thereby reducing surface blushing. (180°F – 220°F)
- Mold Temperature Regulation
Most molding thermolators use hot water as their medium. In the case of elevated mold temperatures as shown above, oil thermolators should be used as they can achieve high temperatures of 220°F and higher without turning to steam.