Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Information (Extrusion Blow Molding)
- Impact Properties
- Injection Molding
- Note
- ʰ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹⁰ Processing parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 66 | MPa | ASTM D638 |
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 7 | % | ASTM D638 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 110 | % | ASTM D638 |
Tensile Modulus (at 5 mm/min) ¹¹ | 2340 | MPa | ASTM D638 |
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 93 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2340 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.20E+00 | — | ASTM D792 |
Mold Shrinkage (flow, 3.2 mm) ʰ ¹¹ | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 2.5 | g/10 min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature (Rate B/50) ¹¹ | 157 | °C | ASTM D1525 |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 138 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 132 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000068 | 1/°C | ASTM E831 |
Value | Units | Test Method / Conditions | |
Drying Temperature ¹⁰ | 120 | °C | — |
Drying Time ¹⁰ | 2 - 4 | Hrs | — |
Maximum Moisture Content ¹⁰ | 0.02 | % | — |
Minimum Moisture Content ¹⁰ | 0.01 | % | — |
Melt Temperature (Parison) ¹⁰ | 265 - 280 | °C | — |
Barrel - Zone 1 Temperature ¹⁰ | 260 - 290 | °C | — |
Barrel - Zone 2 Temperature ¹⁰ | 260 - 290 | °C | — |
Barrel - Zone 3 Temperature ¹⁰ | 260 - 290 | °C | — |
Barrel - Zone 4 Temperature ¹⁰ | 260 - 290 | °C | — |
Adapter - Zone 5 Temperature ¹⁰ | 260 - 290 | °C | — |
Mold Temperature ¹⁰ | 60 - 100 | °C | — |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, at 23°C) ¹¹ | 3204 | J/m | ASTM D4812 |
Izod Impact (Notched, at 23°C) ¹¹ | 748 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 120 | °C | — |
Drying Time ⁷ | 3 - 4 | Hrs | — |
Drying Time (Cumulative) ⁷ | 48 | Hrs | — |
Maximum Moisture Content ⁷ | 0.02 | % | — |
Melt Temperature ⁷ | 320 - 345 | °C | — |
Nozzle Temperature ⁷ | 315 - 340 | °C | — |
Front - Zone 3 Temperature ⁷ | 320 - 345 | °C | — |
Middle - Zone 2 Temperature ⁷ | 310 - 330 | °C | — |
Rear - Zone 1 Temperature ⁷ | 300 - 320 | °C | — |
Mold Temperature ⁷ | 80 - 115 | °C | — |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
Screw Speed ⁷ | 40 - 70 | rpm | — |
Shot to Cylinder Size ⁷ | 40 - 60 | % | — |
Vent Depth ⁷ | 0.025 - 0.076 | mm | — |
Packaging & Availability
- Regional Availability