LNP COLORCOMP™ Compound - A1000HC - SABIC's Specialty

Identification & Functionality

Features & Benefits

Labeling Claims: No Added PFAS
Materials Features: Excellent Aesthetics,
Good Aesthetics,
Good Surface Appearance,
High Durability,
No Added PFAS,
Unreinforced

Applications & Uses

Markets: Healthcare & Pharma,
Printing & Packaging
Applications: Healthcare & Pharma — Medical
Medical Devices & Assemblies,
Surgical Instruments & Trays
Printing & Packaging — Packaging
Healthcare Packaging,
Industrial & Transport Packaging
Plastics & Elastomers End Uses: Medical Devices,
Medical Packaging,
Medical/Healthcare Applications,
Pharmaceutical Packaging,
Surgical Devices
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Color: Custom
Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Note: ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	44	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	33	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	2	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	24	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	2270	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	72	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2340	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	50	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	35	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	2.6	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	24.8	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2530	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	76	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2410	MPa	ISO 178

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.05	—	ASTM D792
Melt Flow Rate (at 230°C, 3.8 kg) ¹¹	5.6	g/10 min	ASTM D1238
Melt Viscosity (at 240°C, 1000 sec⁻¹) ¹¹	2300	Poise	ASTM D3825
Density ¹¹	1.05	g/cm³	ISO 1183
Water Absorption (at 23°C, saturated) ¹¹	1	%	ISO 62-1
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.2	%	ISO 62
Melt Flow Rate (at 220°C, 10.0 kg) ¹¹	19	g/10 min	ISO 1133
Melt Volume Rate (at 220°C, 5.0 kg) ¹¹	14	cm³/10 min	ISO 1133

	Value	Units	Test Method / Conditions
Vicat Softening Temperature (Rate B/50) ¹¹	98	°C	ASTM D1525
Vicat Softening Temperature (Rate B/50) ¹¹	100	°C	ISO 306
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	94	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	80	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000882	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000882	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000882	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000882	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate B/120) ¹¹	100	°C	ISO 306
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	80	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	320	J/m	ASTM D256
Izod Impact (Notched, at -30°C) ¹¹	133	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	30	J	ASTM D3763
Izod Impact (Notched, 80104, at 23°C) ¹¹	23	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80104, at -30°C) ¹¹	8	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80104 sp=62mm) ¹¹	18	kJ/m²	ISO 179/1eA

Packaging & Availability

LNP™ COLORCOMP™ Compound A1000HC