Properties
- Color
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, 5 mm/min) ¹¹ | 52 | MPa | ISO 527 |
Tensile Strain (Yield, 5 mm/min) ¹¹ | 2 | % | ISO 527 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 15 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹¹ | 2500 | MPa | ISO 527 |
Flexural Stress ¹¹ | 75 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹¹ | 2600 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.06 | — | ASTM D792 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.4 - 0.6 | % | ISO 294 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.4 - 0.6 | % | ISO 294 |
Melt Volume Rate (at 220°C, 10.0 kg) ¹¹ | 16 | cm³/10 min | ISO 1133 |
Melt Volume Rate (at 230°C, 10.0 kg) ¹¹ | 27 | cm³/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
Relative Temperature Index (Electrical) ᵖ ¹¹ | 80 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 80 | °C | UL 746B |
Value | Units | Test Method / Conditions | |
Volume Resistivity ¹¹ | 1.00E+16 | Ω.cm | IEC 60093 |
Surface Resistivity (ROA) ¹¹ | 1.00E+16 | Ω | IEC 60093 |
Hot Wire Ignition (PLC 4) ¹¹ | min. 1.5 | mm | UL 746A |
High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
High Voltage Arc Track Rate (PLC) ¹¹ | 1 | PLC Code | UL 746A |
Arc Resistance (Tungsten, PLC) ¹¹ | 6 | PLC Code | ASTM D495 |
Value | Units | Test Method / Conditions | |
Charpy Impact (Unnotched, at -30°C) ¹¹ | 70 | kJ/m² | ISO 179/2C |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 12 | kJ/m² | ISO 180/1A |
Charpy Impact (Notched, at 23°C) ¹¹ | 11 | kJ/m² | ISO 179/2C |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 80 | °C | — |
Drying Time ⁷ | 4 | Hrs | — |
Maximum Moisture Content ⁷ | 0.05 - 0.1 | % | — |
Melt Temperature ⁷ | 260 | °C | — |
Front - Zone 3 Temperature ⁷ | 265 - 275 | °C | — |
Middle - Zone 2 Temperature ⁷ | 230 - 245 | °C | — |
Rear - Zone 1 Temperature ⁷ | 205 - 215 | °C | — |
Mold Temperature ⁷ | 70 - 80 | °C | — |
Back Pressure ⁷ | 0.2 - 0.3 | MPa | — |
Screw Speed ⁷ | 30 - 60 | rpm | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |