LNP™ ELCRIN™ WF006NiQ2

Identification & Functionality

Additives Included

Impact Modifier

Chemical Family

Polyesters

Fillers Included

Glass Fiber

Polymer Name

Polybutylene Terephthalate (PBT)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Recycled Polymers

Plastics — Engineering & Specialty Polymers

Polyesters & Copolyesters

Features & Benefits

Labeling Claims

Contains PCR Resin,

No Added PFAS,

Recyclable,

Recycled,

Sustainable

Materials Features

Chemical Resistant,

Good Adhesion,

Good Bonding Strength,

High Flow,

High Stiffness,

Impact Modified,

Recyclable

Applications & Uses

Markets

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Electrical & Electronics — Devices & Assemblies

Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Plastics & Elastomers End Uses

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Flexural Modulus (1.3 mm/min, 50 mm span)⁴⁹	7400	MPa	ASTM D790
Flexural Modulus (2 mm/min)⁴⁹	7900	MPa	ISO 178
Flexural Stress at Break (1.3 mm/min, 50 mm span)⁴⁹	170	MPa	ASTM D790
Flexural Stress at Break (2 mm/min)⁴⁹	168	MPa	ISO 178
Tensile Modulus (1 mm/min)⁴⁹	8600	MPa	ISO 527
Tensile Modulus (5 mm/min)⁴⁹	8700	MPa	ASTM D638
Tensile Strain at Break (5 mm/min)⁴⁹	2.4	%	ISO 527
Tensile Strain at Break (Type I, 5 mm/min)⁴⁹	2.4	%	ASTM D638
Tensile Stress at Break (5 mm/min)⁴⁹	110	MPa	ISO 527
Tensile Stress at Break (Type I, 5 mm/min)⁴⁹	110	MPa	ASTM D638

Physical Properties

	Value	Units	Test Method / Conditions
Density⁴⁹	1.49	g/cm³	ISO 1183
Melt Flow Rate (at 250°C/5.0 kgf)⁴⁹	21	g/10 min	ASTM D1238
Melt Flow Rate (at 275°C/5 kgf)⁴⁹	37	g/10 min	ASTM D1238
Melt Volume Rate (at 250°C/5.0 kg)⁴⁹	15	cm³/10 min	ISO 1133
Melt Volume Rate (at 275°C/5 kg)⁴⁹	29	cm³/10 min	ISO 1133
Moisture Absorption (at 23°C/50% RH/24hrs)⁴⁹	0.07	%	ISO 62-4
Mold Shrinkage - flow¹²,⁴⁹	0.2 - 0.3	%	SABIC method
Mold Shrinkage - xflow¹²,⁴⁹	0.4 - 0.5	%	SABIC method
Specific Gravity⁴⁹	1.5	-	ASTM D792

Thermal Properties

	Value	Units	Test Method / Conditions
Vicat Softening Temperature Rate (B/120)⁴⁹	0.000105	°C	ASTM D1525 (ISO 306)
Vicat Softening Temperature Rate (B/50)⁴⁹	0.000105	°C	ASTM D1525 (ISO 306)
CTE - flow (at -40°C to 40°C)⁴⁹	2.4e-05	1/°C	ASTM E831
CTE - xflow (at -40°C to 40°C)⁴⁹	0.00013	1/°C	ASTM E831
HDT - Unannealed (0.45 MPa, 3.2 mm)⁴⁹	215	°C	ASTM D648
HDT - Unannealed (1.82 MPa, 3.2mm)⁴⁹	172	°C	ASTM D648
HDT/Af (1.8 MPa Flatw 80*10*4 sp=64mm)⁴⁹	188	°C	ISO 75/Af
HDT/Bf (0.45 MPa Flatw 80*10*4 sp=64mm)⁴⁹	216	°C	ISO 75/Bf

Impact Properties

	Value	Units	Test Method / Conditions
Charpy (at 23°C, V-notch Edgew 80*10*3 sp=62mm)⁴⁹	13	kJ/m²	ISO 179/1eA
Charpy (at -30°C, V-notch Edgew 80*10*3 sp=62mm)⁴⁹	11	kJ/m²	ISO 179/1eA
Charpy (Unnotch Edgew, at 23°C, 80*10*3 sp=62mm)⁴⁹	52	kJ/m²	ISO 179/1eU
Izod Impact Notched (80*10*4 +23°C)⁴⁹	13	kJ/m²	ISO 180/1A
Izod Impact Notched (80*10*4 -30°C)⁴⁹	8	kJ/m²	ISO 180/1A
Izod Impact Notched (at 23°C)⁴⁹	131	J/m	ASTM D256
Izod Impact Notched (at -30°C)⁴⁹	90	J/m	ASTM D256
Izod Impact Unnotched (80*10*4 +23°C)⁴⁹	45	kJ/m²	ISO 180/1U
Izod Impact Unnotched (at 23°C)⁴⁹	750	J/m	ASTM D4812

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature⁴²	100 - 120	°C	—
Drying Time (Cumulative)⁴²	8	Hrs	—
Drying Time⁴²	2 - 4	Hrs	—
Front - Zone 3 Temperature⁴²	250 - 270	°C	—
Hopper Temperature⁴²	40 - 60	°C	—
Maximum Moisture Content⁴²	0.02	%	—
Melt Temperature⁴²	250 - 270	°C	—
Middle - Zone 2 Temperature⁴²	250 - 270	°C	—
Mold Temperature²²	140 - 160	°C	—
Nozzle Temperature⁴²	245 - 275	°C	—
Rear - Zone 1 Temperature⁴²	240 - 260	°C	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized 94HB Flame Class Rating⁵⁹	min. 0.7	mm	UL 94

Note

• ⁴² Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ²² Suggest to use narrow mold temperature 140C~160C for NMT application. Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ⁴⁹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
• ⁵⁹ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ¹² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Asia
• Europe
• North America