LNP™ LUBRICOMP™ Compound CX94108

Identification & Functionality

Additives Included

Lubricant (Unspecified),

Proprietary

Chemical Family

Styrenics

Polymer Name

Polystyrene (unspecified)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Styrenics

Features & Benefits

Materials Features

Lubricated,

Unreinforced,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Industrial

Applications

Building & Construction — Building Envelope & Roofing

Glazing & Window Elements

Building & Construction — Building Materials

Interior Fixtures,

Pipes & Plumbing

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Plastics & Elastomers End Uses

Building Materials,

Construction Applications,

Faucet System Components,

Fittings,

Gears,

Hoses,

Housings,

Pipes,

Pump Parts,

Water Management,

Water Pumps

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	41	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.8	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	3600	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	72	MPa	ISO 178
Flexural Stress (Break, 2 mm/min) ¹¹	69	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	3500	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹	0.6 - 0.8	%	SABIC method
Wear Factor Washer ¹¹	365	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.6	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.71	—	ASTM D3702 Modified: Manual
Density ¹¹	1.08	g/cm³	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	86	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	80	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	10	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	2	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	250	°C	—
Front - Zone 3 Temperature ⁷	265 - 275	°C	—
Middle - Zone 2 Temperature ⁷	245 - 255	°C	—
Rear - Zone 1 Temperature ⁷	220 - 230	°C	—
Mold Temperature ⁷	40 - 65	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 