LNP™ LUBRICOMP™ Compound DX00467H

Identification & Functionality

Additives Included

Lubricant (Unspecified),

Proprietary

Chemical Family

Polycarbonate (PC)

Fillers Included

Silicone Oil

Polymer Name

Polycarbonate (PC)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics,

Polycarbonates

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Friction Resistant,

Lubricated,

No Added PFAS,

Unreinforced,

Wear Resistant

Applications & Uses

Markets

Healthcare & Pharma,

Printing & Packaging

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies,

Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging,

Industrial & Transport Packaging

Plastics & Elastomers End Uses

Medical Devices,

Medical Packaging,

Medical/Healthcare Applications,

Pharmaceutical Packaging,

Surgical Devices

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	62	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	49	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	6	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	59	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	2260	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	91	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2220	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	61	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	50	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	6	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	117	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2040	MPa	ISO 527
Flexural Stress ¹¹	84	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2070	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.19	—	ASTM D792
Density ¹¹	1.18	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.32	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.81	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.99	%	ASTM D955
Wear Factor Washer ¹¹	789	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Wear Factor Ring ¹¹	0	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.19	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.22	—	ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.15	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	137	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	125	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000008	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000008	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	137	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	124	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	1740	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	696	J/m	ASTM D256
Multi-Axial Impact ¹¹	30	J	ISO 6603
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	42	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	203	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	56	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	305 - 325	°C	—
Front - Zone 3 Temperature ⁷	320 - 330	°C	—
Middle - Zone 2 Temperature ⁷	310 - 320	°C	—
Rear - Zone 1 Temperature ⁷	295 - 305	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Packaging & Availability

Regional Availability

• Americas
• Asia
• Europe
• North America