LNP™ LUBRILOY™ Compound DF206XXH

Identification & Functionality

Additives Included

Impact Modifier,

Lubricant (Unspecified),

Mold Release Agent,

Proprietary

Chemical Family

Polycarbonate (PC)

Fillers Included

Glass Fiber

Polymer Name

Polycarbonate (PC)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics,

Polycarbonates

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Friction Resistant,

Good Mold Release,

Impact Modified,

Lubricated,

No Added PFAS,

Wear Resistant

Applications & Uses

Markets

Healthcare & Pharma,

Printing & Packaging

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies,

Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging,

Industrial & Transport Packaging

Plastics & Elastomers End Uses

Medical Devices,

Medical Packaging,

Medical/Healthcare Applications,

Pharmaceutical Packaging,

Surgical Devices

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	112	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.6	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	8240	MPa	ISO 527
Flexural Strength (at 2 mm/min) ¹¹	166	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	7580	MPa	ISO 178
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	112	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.6	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	8720	MPa	ASTM D638
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	174	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	7830	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.16	%	ISO 62
Specific Gravity ¹¹	1.4	—	ASTM D792
Density ¹¹	1.39	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.11	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.4 - 0.6	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.5 - 0.7	%	ASTM D955
Wear Factor Washer ¹¹	245	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Wear Factor Ring ¹¹	27	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.49	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.64	—	ASTM D3702 Modified: Manual

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	141	°C	ISO 75/Af
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	145	°C	ISO 75/Bf
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	142	°C	ASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	146	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000051	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000056	1/°C	ASTM D696

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	17	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	49	kJ/m²	ISO 180/1U
Multi-Axial Impact ¹¹	6	J	ISO 6603
Izod Impact (Notched, at 23°C) ¹¹	178	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	775	J/m	ASTM D4812
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	26	J	ASTM D3763

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	100	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	290 - 315	°C	—
Front - Zone 3 Temperature ⁷	280 - 310	°C	—
Middle - Zone 2 Temperature ⁷	280 - 300	°C	—
Rear - Zone 1 Temperature ⁷	275 - 300	°C	—
Mold Temperature ⁷	65 - 95	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 