LNP™ STAT-LOY™ Compound A3000

Identification & Functionality

Additives Included

Anti-Static Agent

Chemical Family

Acrylonitrile Butadiene Styrene (ABS),

Styrenics

Fillers Included

Proprietary

Polymer Name

Acrylonitrile Butadiene Styrene (ABS)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Styrenics

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Anti-Static,

No Added PFAS,

Unreinforced

Applications & Uses

Markets

Electrical & Electronics,

Industrial

Applications

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Plastics & Elastomers End Uses

Computer Components,

Electrical/Electronic Applications,

Industrial Applications,

Semiconductor Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	39	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	36	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	3.1	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	6	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	2060	MPa	ASTM D638
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	65	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2090	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	38	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	31	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	3	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	24.2	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2010	MPa	ISO 527
Flexural Strength (at 2 mm/min) ¹¹	59	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	1980	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.06	g/cm³	ISO 1183
Density ¹¹	1.065	g/cm³	ASTM D792
Melt Flow Rate (at 230°C, 5 kgf) ¹¹	19	g/10 min	ASTM D1238
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	1.08	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.41	%	ISO 294
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.4	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.5	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.49	%	ISO 294

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	88	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	76	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000934	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000101	1/°C	ASTM E831
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.0000934	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000101	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	91	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	76	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	6.00E+01	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	60	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	60	°C	UL 746B

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity ¹¹	1000000000 - 100000000000	Ω	ASTM D257

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	No break	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	282	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	32	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	No break	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	20	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	70 - 80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.05 - 0.1	%	—
Melt Temperature ⁷	200 - 210	°C	—
Front - Zone 3 Temperature ⁷	205 - 215	°C	—
Middle - Zone 2 Temperature ⁷	195 - 205	°C	—
Rear - Zone 1 Temperature ⁷	180 - 195	°C	—
Mold Temperature ⁷	10 - 50	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	1.5	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA