Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.44 | g/cm³ | ISO 1183 |
Mold Shrinkage (flow) ᵍ ¹¹ | 0.13 | % | SABIC method |
Mold Shrinkage (xflow) ᵍ ¹¹ | 0.16 | % | SABIC method |
Specific Gravity ¹¹ | 1.44 | — | ASTM D792 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 0.02 | % | ASTM D570 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.25 - 0.7 | % | SABIC method |
Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ | 29.1 | g/10 min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Flexural Modulus (at 2 mm/min) ¹¹ | 8110 | MPa | ISO 178 |
Tensile Modulus (at 1 mm/min) ¹¹ | 6640 | MPa | ISO 527 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 1.5 | % | ISO 527 |
Flexural Stress (Break, 2 mm/min) ¹¹ | 170 | MPa | ISO 178 |
Tensile Stress (Break, 5 mm/min) ¹¹ | 120 | MPa | ISO 527 |
Tensile Stress (Yield) ¹¹ | 112 | MPa | SABIC - Japan Method |
Tensile Strain (Break) ¹¹ | 8 | % | SABIC - Japan Method |
Flexural Stress ¹¹ | 156 | MPa | ASTM D790 |
Flexural Modulus ¹¹ | 8430 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 264 | °C | ISO 75/Bf |
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 267 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.000025 - 0.000055 | 1/°C | TMA |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index ¹¹ | 150 | V | IEC 60112 |
Volume Resistivity ¹¹ | 1.20E+17 | Ω.cm | ASTM D257 |
Surface Resistivity ¹¹ | 1.00E+16 | Ω | ASTM D257 |
Dielectric Strength (in oil, at 1.6mm) ¹¹ | 22.1 | kV/mm | ASTM D149 |
Relative Permittivity (50/60 Hz) ¹¹ | 3.3 | — | ASTM D150 |
Value | Units | Test Method / Conditions | |
Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 22 | kJ/m² | ISO 179/1eU |
Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 6 | kJ/m² | ISO 179/1eA |
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 59 | kJ/m² | ISO 179/1eU |
Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 21 | kJ/m² | ISO 179/1eA |
Izod Impact (Notched, at 23°C) ¹¹ | 88 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 120 - 150 | °C | — |
Drying Time ⁷ | 4 - 8 | Hrs | — |
Drying Time (Cumulative) ⁷ | 24 | Hrs | — |
Maximum Moisture Content ⁷ | 0.02 | % | — |
Melt Temperature ⁷ | 300 - 330 | °C | — |
Nozzle Temperature ⁷ | 300 - 330 | °C | — |
Front - Zone 3 Temperature ⁷ | 295 - 330 | °C | — |
Middle - Zone 2 Temperature ⁷ | 290 - 320 | °C | — |
Rear - Zone 1 Temperature ⁷ | 280 - 315 | °C | — |
Mold Temperature ⁷ | 95 - 150 | °C | — |
Back Pressure ⁷ | 0.7 - 1.4 | MPa | — |
Screw Speed ⁷ | 50 - 100 | rpm | — |
Shot to Cylinder Size ⁷ | 40 - 60 | % | — |
Vent Depth ⁷ | 0.025 - 0.076 | mm | — |