Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Note
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 70 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 70 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 5 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 5 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2540 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 107 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2580 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Density ¹¹ | 1.06 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.25 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.06 | % | ISO 62 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 40 | cm³/10 min | ISO 1133 |
| Melt Viscosity (at 280°C, 1500 sec⁻¹) ¹¹ | 133 | Pa-s | ISO 11443 |
| Value | Units | Test Method / Conditions | |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate A/120) ¹¹ | 151 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 143 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 145 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 125 | °C | ISO 75/Af |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 4 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 2 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 4 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 3 | kJ/m² | ISO 179/1eA |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁷ | 80 - 100 | °C | — |
| Drying Time ⁷ | 2 - 4 | Hrs | — |
| Melt Temperature ⁷ | 280 - 300 | °C | — |
| Nozzle Temperature ⁷ | 260 - 280 | °C | — |
| Front - Zone 3 Temperature ⁷ | 280 - 300 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 260 - 280 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 240 - 260 | °C | — |
| Hopper Temperature ⁷ | 60 - 80 | °C | — |
| Mold Temperature ⁷ | 60 - 100 | °C | — |
Packaging & Availability