Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Information (Extrusion Blow Molding)
- Impact Properties
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 83 | % | ASTM D638 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 95 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2270 | MPa | ASTM D790 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.09 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 1.3 - 1.4 | % | SABIC method |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 179 | °C | ASTM D648 |
| Value | Units | Test Method / Conditions | |
| Adapter - Zone 5 Temperature | 275 - 290 | °C | — |
| Barrel - Zone 1 Temperature | 270 - 280 | °C | — |
| Barrel - Zone 2 Temperature | 270 - 280 | °C | — |
| Barrel - Zone 3 Temperature | 270 - 280 | °C | — |
| Barrel - Zone 4 Temperature | 270 - 280 | °C | — |
| Die Temperature | 275 - 290 | °C | — |
| Drying Temperature | 80 | °C | — |
| Drying Time | 4 | Hrs | — |
| Drying Time (Cumulative) | 16 | Hrs | — |
| Head - Zone 6 - Top Temperature | 275 - 290 | °C | — |
| Head - Zone 7 - Bottom Temperature | 275 - 290 | °C | — |
| Melt Temperature (Parison) | 275 - 290 | °C | — |
| Mold Temperature | 80 | °C | — |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Notched, at 23°C) ¹¹ | 336 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 1.22E+02 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 31 | J | ASTM D3763 |
| Instrumented Dart Impact Energy (Peak, at -30°C) ¹¹ | 36 | J | ASTM D3763 |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |