- Flexible, abrasion resistant, durable surface - The Forming Grade Mar-Con 551 coated surface, more abrasion resistant than the base plastic, reduces risk of damage to the sheet surfaces from frequent cleaning and handling.
- Superior chemical and solvent resistance - Reduces risk of solvent or chemical damage to the sheet surfaces.
- Excellent optical properties - High clarity, high gloss coating maintains optimum light transmission without distortion.
- Advanced technology, uniform surface treatment - Provides enhanced abrasion and chemical resistance without changing the appearance of the acrylic surfaces.
- Graffiti resistance - Easy to clean hydrophobic surface
- Superior fabrication and bending characteristics - Results in optimum heat forming during part fabrication
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Applications
Mar-Con® 551 Acrylic - Forming Grade is designed to be used where there is concern about abrasion of the surfaces of the plastic sheet from handling and other moderate abuse. It is also designed for applications requiring improved splash and wipe down resistance to many common chemicals and solvents which would normally damage the acrylic sheet surfaces. The Forming Grade Mar-Con® 551 coated surface helps prevent such damage from short-term exposures to these materials. Typical applications for Mar-Con® 551 Acrylic - Forming Grade include formed fabricated items, such as: equipment covers, display components, safety shields, and curved machine guards.
- Fabrication
Mar-Con® 551 Acrylic - Forming Grade is easily fabricated into a variety of flat and bent surface configurations using the same equipment employed with uncoated acrylic sheet products. The product is designed to accommodate drape forming and heat bending, however, care must be taken to avoid applying too much heat to prevent damage to the abrasion resistant coating. Soft radii shapes and bends can be achieved which are smooth, clear, and uniform, if recommended forming techniques are employed. Some distortion and loss of abrasion resistance in a bend area is normal. On tight bends, particularly in thicker materials, there may be some very fine haze lines in the bend area. When solvent welding, it is necessary to remove the Mar-Con 551 coated surface mechanically to achieve a good bond.
- Cleaning
The Forming Grade Mar-Con 551 coated surface can be cleaned with a variety of common cleaners (see reverse side for specific recommendations). Care should be taken to avoid the use of any cleaner or cleaning solution which contains an abrasive. In addition, all wipes, sponges, and drying towels should be clean and free of any grit which could damage the surface.
- Cleaning and Graffiti Removal
Solvents and Cleaning Liquids Found Effective Under Laboratory Conditions
Aqueous solutions of the following can be applied carefully with a soft cloth or sponge for ordinary dirt and grime.Joy® Windex® Formula 409® Sparkle™ Rinse with clean water before drying with a chamois or cellulose sponge.
Never use an abrasive cleaner or scouring pad.
The following solvents, in addition to the above cleaners, can be used to remove graffiti and other stubborn stains.
Isopropyl Alcohol-Methanol
Naphtha (VM&P Grade)-Kerosene
Butyl Cellosolve (for paints, inks, lipstick, etc.)
Always remove residual solvent with an aqueous cleaner and a final rinse with clean water.
Properties
- Physical Form
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Optical Properties
- Flammability
| Value | Units | Test Method / Conditions | |
| Compressive Strength | 18000.0 | psi | ASTM D695 |
| Flexural Modulus | 475000.0 | psi | ASTM D790 |
| Flexural Strength | 16500.0 | psi | ASTM D790 |
| Izod Impact Strength (milled notch) | 0.4 | ft-lb/inch | ASTM D256 |
| Tensile Modulus | 400000.0 | psi | ASTM D638 |
| Tensile Strength Elongation | 4.2 | % | ASTM D638 |
| Tensile Strength Ultimate | 10000.0 | psi | ASTM D638 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 1.19 | - | ASTM D792 |
| Taber Abrasion1 - ∆ Haze | max. 8 | % | ASTM D1044 |
| Weighted Steel Wool Rub Resistance2 | Light Scratches | - | Internal |
| Value | Units | Test Method / Conditions | |
| Coefficient of Thermal Conductivity | 1.3 | BTU.in/hr.ft2.°F | Cenco-Fitch |
| Coefficient of Thermal Expansion | 3.8 x 10^-5 | in/in/°F | ASTM D696 |
| Deflection Temperature (264 psi load) | 210.0 | °F | ASTM D648 |
| Maximum Continuous Service Temperature | 180.0 | °F | - |
| Vicat Softening Point | 239.0 | °F | ASTM D1525 |
| Value | Units | Test Method / Conditions | |
| Haze | max. 1.0 | % | ASTM D1003 |
| Transmittance, 3mm Transparent Clear - Total | 92.0 | % | ASTM D1003 |
| Value | Units | Test Method / Conditions | |
| Horizontal Burn (Flame Spread) | 1.1 | in/min | ASTM D635 |
| UL 94 Rating of the Uncoated Substrate | HB | - | UL 94 |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Chemical Resistance ASTM D-1308
Samples immersed in listed chemicals and then examined for visible attack at 15 minutes, 1 hour, and 24 hours.
Chemical Time for visible Attack
Acetone < 1 hour Methyl Alcohol > 24 hours Isopropyl Alcohol > 24 hours Kerosene > 24 hours Toluene < 1 hour Sodium Hydroxide (10%) > 24 hours Hydrochloric Acid (10%) > 24 hours Sulfuric Acid (10%) > 24 hours Nitric Acid (10%) > 24 hours
Packaging & Availability
- Availability
Mar-Con® 551 Acrylic - Forming Grade, in cell cast type, is available in clear and a variety of standard transparent colors. White translucent and colored opaque grades are also available. Continuously cast, extruded types and impact modified types are available in some sizes and thicknesses upon request.
Note: Cell cast is a premium acrylic plastic, but it has a wider thickness variation than other acrylic types. Therefore, continuously cast or extruded material should be specified if a narrow thickness tolerance range is needed.
Standard Dimensions (Nominal)
Thickness: 3mm (1/8”), 4.5mm (3/16”), 6mm (1/4”), 9mm (3/8”), 12mm (1/2”) - Note: 9mm and 12mm - cell cast only.
Standard Sheet Size: 48” x 96”
Other sizes and thicknesses available upon request.