Value | Units | Test Method / Conditions | |
Tensile Strength | 2870 | psi | ASTM D412 Method A |
Ultimate Elongation | 79 | % | — |
Stress at Elongation (M25) | 1184 | psi | — |
Stress at Elongation (M50) | 1708 | psi | — |
Stress at Elongation (M100) | 1740 | psi | — |
Strain Energy at 20% elongation | 188 | psi | — |
Calculated Shear Modulus, G | 3525 | psi | — |
Calculated Youngs Modulus, E | 10575 | psi | — |
E-secant from the initial slope | 9940 | psi | — |
Tear Strength | 221 | lbf/inch | ASTM D624, Die B |
Durometer Hardness | max. 95 | points | ASTM D2240, Type A |
Durometer Hardness | min. 92 | points | ASTM D2240, Type A |
Specific Gravity | 1.91 | — | ASTM D297, 15 |
Compression Set (22 hrs at 392°F) | 15 | % | ASTM D395, Test B |
Compression Set (70 hrs at 392°F) | 22 | % | ASTM D395, Test B |
Compression Set (336 hrs at 392°F) | 37 | % | ASTM D395, Test B |
Change in Tensile (70 hrs at 392°F) | 2 | % | ASTM D865 |
Change in Tensile (168 hrs at 392°F) | -2 | % | ASTM D865 |
Change in Tensile (336 hrs at 392°F) | 8 | % | ASTM D865 |
Change in Tensile (1000 hrs at 392°F) | -12 | % | ASTM D865 |
Change in Elongation (70 hrs at 392°F) | -4 | % | ASTM D865 |
Change in Elongation (168 hrs at 392°F) | -8 | % | ASTM D865 |
Change in Elongation (336 hrs at 392°F) | -5 | % | ASTM D865 |
Change in Elongation (1000 hrs at 392°F) | -22 | % | ASTM D865 |
Change in Durometer (70 hrs at 392°F) | 2 | points | ASTM D865 |
Change in Durometer (168 hrs at 392°F) | 1 | points | ASTM D865 |
Change in Durometer (336 hrs at 392°F) | 1 | points | ASTM D865 |
Change in Durometer (1000 hrs at 392°F) | 1 | points | ASTM D865 |
Glass Transition | -4 | °F | ASTM D1329 |