Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Dielectric Loss Factor (50Hz, 20°C) | 5×10^-4 | — | GB/T1409 |
Dielectric Strength | 38.0 | MV/m | GB/T1408.1 |
Elongation at Break | 487.0 | % | GB/T1040.3 |
Impact Brittle Temperature (-76°C) | Pass | — | GB/T5470 |
Maximum Elongation at Break Change (Test temperature 135°C, 168 hr) | 3.7 | % | GB/T8815 |
Maximum Elongation at Break Change (Ageing after 42 Days Vs. after 21 Days) | -8.0 | % | GB/T2951 |
Maximum Elongation at Break Change (Ageing after 42days) | -25.0 | % | GB/T2951 |
Maximum Elongation Change under Load (200±3°C x 15 min x 0.2 MPa) | 48.0 | % | GB/T2951 |
Maximum Permanent Elongation Change after Cooled (200±3°C x 15 min x 0.2 MPa) | -4.0 | % | GB/T2951 |
Maximum Tensile Strength Change (Ageing after 42 Days Vs. after 21 Days) | -2.0 | % | GB/T2951 |
Maximum Tensile Strength Change (Ageing after 42days) | -18.0 | % | GB/T2951 |
Maximum Tensile Strength Change (Test temperature 135°C, 168 hr) | 8.9 | % | GB/T8815 |
Pressure Crack Test F50 | Pass | hr | GB/T2951 |
Tensile Strength | 23.6 | MPa | GB/T1040.3 |
Volume Resistance (20°C) | 1×10^14 | Ohm.m | GB/T1410 |