Electric/Electronic Applications(TV,Monitor Housing) IT/OA device
Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Flammability
- Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 1.19 | — | ASTM D792 |
| Molding Shrinkage(Flow) (3.2mm) | 0.4 ~ 0.7 | % | ASTM D955 |
| Melt Flow Rate (220°C/10kg) | 8.0 | g/10min | ASTM D1238 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (3.2mm) (50mm/min) | 400.0 | kg/cm2 | ASTM D638 |
| Tensile Elongation at Break (3.2mm) (50mm/min) | 20.0 | % | ASTM D638 |
| Tensile Elongation at Break (3.2mm) (50mm/min) | 5.0 | % | ASTM D638 |
| Tensile Modulus (3.2mm) (1mm/min) | 20000.0 | kg/cm2 | ASTM D638 |
| Flexural Modulus (6.4mm) (15mm/min) | 23000.0 | kg/cm2 | ASTM D790 |
| Flexural Modulus (6.4mm) (15mm/min) | 680.0 | kg/cm2 | ASTM D790 |
| IZOD Impact Strength (6.4mm) (Notched) (-30°C) | 4 | kg.cm/cm | ASTM D256 |
| IZOD Impact Strength (6.4mm) (Notched) (23°C) | 9 | kg.cm/cm | ASTM D256 |
| IZOD Impact Strength (3.2mm) (Notched) (-30°C) | 6 | kg.cm/cm | ASTM D256 |
| IZOD Impact Strength (3.2mm) (Notched) (23°C) | 18 | kg.cm/cm | ASTM D256 |
| Rockwell Hardness (R-Scale) | 100.0 | — | ASTM D785 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (6.4mm) (Unannealed) (18.6kg - 4.6 kg) | 91 - 102 | °C | ASTM D648 |
| Vicat Softening Temperature (5kg .50°C/h) | 100.0 | °C | ASTM D1525 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 70 ~ 80 | °C | — |
| Back Pressure | 5 ~ 10 | kg/cm2 | — |
| 1.5mm | V-0 | class | — |
| 2.0mm | V-0,5VA | class | — |
| 3.0mm | V-0,5VA | class | — |
| Relative Temperature Index Electrical | 85.0 | °C | UL746B |
| Relative Temperature Index Mechanical with lmpact | 85.0 | °C | UL746B |
| Relative Temperature Index Mechanical without lmpact | 85.0 | °C | UL746B |
| Value | Units | Test Method / Conditions | |
| Drying Time | 2 ~ 4 | hrs | — |
| Moisture Content | min. 0.01 | % | — |
| Melt Temperature | 200 ~ 230 | °C | — |
| Cylinder Temperature Rear | 170 ~ 190 | °C | — |
| Cylinder Temperature Middle | 180 ~ 200 | °C | — |
| Cylinder Temperature Front | 190 ~ 210 | °C | — |
| Nozzle Temperature | 200 ~ 230 | °C | — |
| Mold Tempeature | 40 ~ 60 | °C | — |
| Screw Speed | 30 ~ 60 | rpm | — |