Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Application
Electric/Electronic Applications(TV,Monitor Housing) IT/OA device
Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Flammability
- Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.19 | — | ASTM D792 |
Molding Shrinkage(Flow) (3.2mm) | 0.4 ~ 0.7 | % | ASTM D955 |
Melt Flow Rate (220°C/10kg) | 37.0 | g/10min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Tensile Strength at Yield (3.2mm) (50mm/min) | 450.0 | kg/cm2 | ASTM D638 |
Tensile Elongation at Break (3.2mm) (50mm/min) | 20.0 | % | ASTM D638 |
Tensile Elongation at Break (3.2mm) (50mm/min) | 5.0 | % | ASTM D638 |
Tensile Modulus (3.2mm) (1mm/min) | 22000.0 | kg/cm2 | ASTM D638 |
Flexural Modulus (6.4mm) (15mm/min) | 24000.0 | kg/cm2 | ASTM D790 |
Flexural Modulus (6.4mm) (15mm/min) | 700.0 | kg/cm2 | ASTM D790 |
IZOD Impact Strength (6.4mm) (Notched) (23°C) | 18 | kg.cm/cm | ASTM D256 |
IZOD Impact Strength (6.4mm) (Notched) (-30°C) | 6 | kg.cm/cm | ASTM D256 |
IZOD Impact Strength (3.2mm) (Notched) (-30°C) | 6 | kg.cm/cm | ASTM D256 |
IZOD Impact Strength (3.2mm) (Notched) (23°C) | 21 | kg.cm/cm | ASTM D256 |
Rockwell Hardness (R-Scale) | 103.0 | — | ASTM D785 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (6.4mm) (Unannealed) (18.6kg - 4.6 kg) | 81 - 89 | °C | ASTM D648 |
Vicat Softening Temperature (5kg .50°C/h) | 88.0 | °C | ASTM D1525 |
Value | Units | Test Method / Conditions | |
1.5mm | V-0 | class | — |
2.0mm | V-0,5VB | class | — |
2.5mm | V-0,5VB | class | — |
3.0mm | V-0,5VB | class | — |
Relative Temperature Index Electrical | 60.0 | °C | UL746B |
Relative Temperature Index Mechanical with lmpact | 60.0 | °C | UL746B |
Relative Temperature Index Mechanical without lmpact | 60.0 | °C | UL746B |
Value | Units | Test Method / Conditions | |
Drying Temperature | 70 ~ 80 | °C | — |
Drying Time | 2 ~ 4 | hrs | — |
Moisture Content | min. 0.01 | % | — |
Melt Temperature | 200 ~ 230 | °C | — |
Cylinder Temperature Rear | 170 ~ 190 | °C | — |
Cylinder Temperature Middle | 180 ~ 200 | °C | — |
Cylinder Temperature Front | 190 ~ 210 | °C | — |
Nozzle Temperature | 200 ~ 230 | °C | — |
Mold Tempeature | 40 ~ 60 | °C | — |
Back Pressure | 5 ~ 10 | kg/cm2 | — |
Screw Speed | 30 ~ 60 | rpm | — |