Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Application
Automotives Interior&Exterior Housing(garnish etc)
Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.05 | - | ASTM D792 |
Molding Shrinkage(Flow) (3.2mm) | 0.4 ~ 0.7 | % | ASTM D955 |
Melt Flow Rate (220°C/10kg) | 15.0 | g/10min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Tensile Strength at Yield (3.2mm) (50mm/min) | 480.0 | kg/cm2 | ASTM D638 |
Tensile Elongation at Break (3.2mm) (50mm/min) | 25.0 | % | ASTM D638 |
Tensile Elongation at Break (3.2mm) (50mm/min) | min. 5 | % | ASTM D638 |
Flexural Strength (3.2mm) (15mm/min) | 800.0 | kg/cm2 | ASTM D790 |
Tear Strength at Break (15mm/min) | 26500.0 | kg/cm | ASTM D624 |
IZOD Impact Strength (6.4mm) (Notched) (-30°C) | 10 | kg.cm/cm | ASTM D256 |
IZOD Impact Strength (6.4mm) (Notched) (23°C) | 28 | kg.cm/cm | ASTM D256 |
IZOD Impact Strength (3.2mm) (Notched) (-30°C) | 12 | kg.cm/cm | ASTM D256 |
IZOD Impact Strength (3.2mm) (Notched) (23°C) | 30 | kg.cm/cm | ASTM D256 |
Rockwell Hardness (R-Scale) | 110.0 | - | ASTM D785 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (6.4mm) (Unannealed) (18.6kg - 4.6 kg) | 91 - 99 | °C | ASTM D648 |
Vicat Softening Temperature (5kg .50°C/h) | 99.0 | °C | ASTM D1525 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index(CTI) (Solution A) | 0.0 | Volts | IEC 60112 |
Value | Units | Test Method / Conditions | |
Relative Temperature Index Electrical | 60.0 | °C | UL746B |
Relative Temperature Index Mechanical with lmpact | 60.0 | °C | UL746B |
Relative Temperature Index Mechanical without lmpact | 60.0 | °C | UL746B |
Volume Resistivity (23°C) | 14.0 | Ohm.m | ASTM D257 |
Arc Resistance (23°C) | 6.0 | Ohm.cm | ASTM D495 |
Dielectric Strength (1mm) (23°C) | 30.0 | kV/mm | ASTM D149 |
Value | Units | Test Method / Conditions | |
Drying Temperature | 70 ~ 80 | °C | - |
Drying Time | 3 ~ 4 | hrs | - |
Moisture Content | min. 0.01 | % | - |
Melt Temperature | 200 ~ 230 | °C | - |
Cylinder Temperature Rear | 180 ~ 200 | °C | - |
Cylinder Temperature Middle | 190 ~ 210 | °C | - |
Cylinder Temperature Front | 200 ~ 220 | °C | - |
Nozzle Temperature | 200 ~ 230 | °C | - |
Mold Tempeature | 40 ~ 60 | °C | - |
Back Pressure | 300 ~ 600 | kg/cm2 | - |
Screw Speed | 30 ~ 60 | rpm | - |