Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Application
Electric&Electronic Products(Monitor)
Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 1.04 | - | ASTM D792 |
| Molding Shrinkage(Flow) (3.2mm) | 0.4 ~ 0.7 | % | ASTM D955 |
| Melt Flow Rate (220°C/10kg) | 45.0 | g/10min | ASTM D1238 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (3.2mm) (50mm/min) | 450.0 | kg/cm2 | ASTM D638 |
| Tensile Elongation at Break (3.2mm) (50mm/min) | 21900.0 | % | ASTM D638 |
| Tensile Elongation at Break (3.2mm) (50mm/min) | 30.0 | % | ASTM D638 |
| Tensile Modulus (3.2mm) (1mm/min) | 740.0 | kg/cm2 | ASTM D790 |
| Flexural Strength (3.2mm) (15mm/min) | 26500.0 | kg/cm2 | ASTM D790 |
| IZOD Impact Strength (6.4mm) (Notched) (23°C) | 20 | kg.cm/cm | ASTM D256 |
| IZOD Impact Strength (3.2mm) (Notched) (23°C) | 20 | kg.cm/cm | ASTM D256 |
| Rockwell Hardness (R-Scale) | 109.0 | - | ASTM D785 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (6.4mm) (Unannealed) (18.6kg - 4.6 kg) | 86.0 | °C | ASTM D648 |
| Value | Units | Test Method / Conditions | |
| Comparative Tracking Index(CTI) (Solution A) | 1.0 | Volts | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Relative Temperature Index Electrical | 60.0 | °C | UL746B |
| Relative Temperature Index Mechanical with lmpact | 60.0 | °C | UL746B |
| Relative Temperature Index Mechanical without lmpact | 60.0 | °C | UL746B |
| Arc Resistance (23°C) | 6.0 | Ohm.cm | ASTM D495 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 80.0 | °C | - |
| Drying Time | 2 ~ 4 | hrs | - |
| Moisture Content | min. 0.01 | % | - |
| Melt Temperature | 210 ~ 240 | °C | - |
| Cylinder Temperature Rear | 180 ~ 200 | °C | - |
| Cylinder Temperature Middle | 190 ~ 210 | °C | - |
| Cylinder Temperature Front | 200 ~ 220 | °C | - |
| Nozzle Temperature | 200 ~ 230 | °C | - |
| Mold Tempeature | 40 ~ 70 | °C | - |
| Back Pressure | 300 ~ 600 | kg/cm2 | - |
| Screw Speed | 30 ~ 60 | rpm | - |