Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Typical Properties
- Thermal Properties
| Value | Units | Test Method / Conditions | |
| Flexural Modulus | 1614 | MPa | ISO 178 |
| Tensile Modulus | 1550 | MPa | ISO 527-1, -2 |
| Tensile Stress at Yield | 26 | MPa | ISO 527-1, -2 |
| Tensile Strain at Yield | 4 | % | ISO 527-1, -2 |
| Tensile Strain at Break | 22 | % | ISO 527-1, -2 |
| Charpy Impact Notched, Type 1, Edgewise, Notch A (at 23 °C) | 8.6 | kJ/m² | ISO 179 |
| Charpy Impact Notched, Type 1, Edgewise, Notch A (at 0 °C) | 6.1 | kJ/m² | ISO 179 |
| Charpy Impact Notched, Type 1, Edgewise, Notch A (at -20 °C) | 4.5 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (at 23 °C) | 6.8 | J/m | ISO 180 |
| Value | Units | Test Method / Conditions | |
| Density | 0.9 | g/cm³ | ISO1183-1 |
| Melt Flow Rate (at 230 °C/2.16 kg.) | 19 | g/10 min | ISO1133 |
| Barrel temperature range | 210 -250 | °C | — |
| Mold temperature | 15 -40 | °C | — |
| Melt temperature | 240 -260 | °C | — |
| Mold Shrinkage | 1 – 2.5 | % | — |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature-A, 1.8 MPa, unannealed | 60 | °C | ISO 75B-1, -2 |
| Heat Deflection Temperature -B, 0.45 MPa, unannealed | 102 | °C | ISO 75B-1, -2 |
| Vicat Softening Temperature, A50 | 148 | °C | ISO 306 |
| Vicat Softening Temperature, B50 | 70 | °C | ISO 306 |
Regulatory & Compliance
- Food Contact Regulation
This product complies with the relevant requirements of EU, China, South America & United States Food contact. Declaration of Compliance Certificate are available on our Internet site.
Storage & Handling
- Safety and Handling
The product is not classified as a hazardous material. Polypropylene resin should be stored in a manner to prevent a direct exposure to sunlight and/or heat. The storage area should also be dry and preferably do not exceed 50°C. Sipchem would not give warranty to bad storage conditions which may lead to quality deterioration such as color change, bad smell and inadequate product performance. It is advisable to process PP resin within 6 months after delivery. Conveying equipment should be designed to prevent production and accumulation of fines and dust particles that are contained in polymer resins. These particles can under certain conditions pose an explosion hazard. Conveying systems should be grounded, equipped with adequate filters and regularly inspected for leaks.