Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Features
High elogation, High impact strength, Excellent flexibility.
Applications & Uses
- Applications
- Plastics & Elastomers Processing Methods
- Applications
Cable tie, Automobile fuel lines, Wring harness, Sprocket housing.
- Processing Guidelines
PACKAGING & PRE-DRYING
Synergy's Synlon (Nylon 6 & 66) is packed at maximum moisture content of 0.2% in moisture-proof, lined packaging. However Nylon being hygroscopic, it is advisable to dry the material at 100-120 degree centigrade for 2-4 hours. Natural and lighter shade material may be dried at lesser temp. and lesser duration to avoid discoloration, brittleness due to over heating. Then need for drying the material is evident by the formation of bubbles or foam in the melt, excessive drooling from the nozzle, or streaks in the molded parts.
PROCESSING RECOMMENDATIONS
Synergy's Synlon (Nylon 6 & 66) should be injected at fast injection speeds, to prevent premature crystallization. Low to medium injection pressures is recommended. Faster injection speeds and medium injection pressures provide a longer material flow path in the mold, better packing, good surface appearance, and low molded in stresses.
The Holding or packing pressure should be about 50 to 65% of the injection pressure. The holding pressure should be optimized to effectively control sink marks and flashing. Optimum extruder speed and back pressure must be used to ensure a uniform melt and shot size consistency. Sufficient back pressure ensures homegenous melt formation and elimination of gas voids in the melt. Use of shut-off nozzle is recommended to avoid drooling.
Conditioning : It is advised to condition in hot water at 80-100 Deg. C for 2-4 hrs. depending upon the component thickness and as required by the subsequent process also to release internal stresses if any to avoid breakage druing further assembly.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 1.08 | — | ASTM D-792 |
| Mould Shrinkage | 1.5-2.0 | % | ASTM D-955 |
| Tensil Strength | 55.0 | MPa | ASTM D-638 |
| Elongation at Break | 165.0 | % | ASTM D-638 |
| Flexural Strength | 55.0 | MPa | ASTM D-790 |
| Flexural Modulus | 1250.0 | MPa | ASTM D-790 |
| Izod Impact Strength | 30/190 | kg.cm/cm | ASTM D-256A |
| Heat Deflection Temperature at 18.5 kg/sq.cm. load | 62.0 | °C | ASTM D-648 |
| Heat Deflection Temperature at 4.6 kg/sq.cm.load | 135.0 | °C | ASTM D-648 |
Technical Details & Test Data
- Process Parameters
FEED ZONE TEMPERATURE COMPRESSION ZONE TEMPERATURE METERING ZONE TEMPERATURE NOZZLE TEMPERATURE MELT TEMPERATURE INJECTION PRESSURE KG/CM2 MOLD TEMPERATURE 170 210 215 220 210-225 900-1000 75-95