Knowde Enhanced TDS
Identification & Functionality
- Carrier
- Chemical Family
- CASE Ingredients Functions
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
Applications & Uses
- Applications
- Compatible Substrates & Surfaces
- Cure Method
- Coating Type
- Uses
2-pack coatings which are air- and oven-drying in combination with aliphatic polyisocyanates,
for industrial coatings affording high mechanical strength, good adhesion and resistance to
weathering.- Properties and Fields of use
The main field of application for SYNTHALAT-A 150 is in coatings for metals and plastics which
are air- and oven-drying in combination with aliphatic polyisocyanates. This type of 2-pack
coating is preferred where the size or temperature sensitivity of objects to be coated stands in
the way of achieving the required high-grade coating qualities. Examples are car refinishing,
original finishing of busses and trams, plastic items, etc.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Non Volatile Content | Max. 2 | w % | AV-F-F003 |
| Density | 0.99 | g/ml | AV-F-0D001 |
| Flash point | 30 | °C | AV-F-f006 |
| Flash point | 60 | °C | AV-F-f006 |
| Flow Time | 140-180 | sec | AV-F-V003 |
| Hydroxyl Content | 4.5 | % | Relative to NVC |
| Hydroxyl Content | 130-150 | % | Relative to NVC |
Technical Details & Test Data
- Film Properties
In combination with aliphatic polyisocyanates such as "Desmodur N" they afford non-yellowing
finishes with excellent weather resistance and gloss retention. Such films have good resistance
to scratching and abrasion, combined with good solvent resistance. Their good resistance to
water and aggressive chemicals should also be emphasized. SYNTHALAT-A 150 differs from A
045, A 055, A 065 and A 085 in its higher cross-linking density, which affords films having
significantly greater abrasion and solvent resistance. These values are exceeded only by A 190
with its higher cross-linking density.- Pigmentation
SYNTHALAT-A 150 has high pigment absorption and very good pigment wetting properties.
Any neutral pigments or fillers are suitable for pigmentation. Basic pigments and pigments
containing soluble metal compounds may have a catalytic effect on curing and shorten the pot
life of coating batches once mixed.
Packaging & Availability
- Supplied AS
A = 60% in xylene/shellsol A/ butyl acetate (2:1:1)
B = 60% in butyl acetat